This Standard specifies hexagon nuts and hexagon thin nuts (hereafter generically referred to as "hexagon nuts") made of steel, stainless steel and non-ferrous metals.
If, in special cases, dimensions and product specifications other than those listed in this Standard are required, they shall be selected from existing Japanese Industrial Standards, for example JIS B 0205-4, JIS B 0209-1, JIS B 1021, JIS B 1052-2, JIS B 1052-6 and JIS B 1054-2 upon agreement between the purchaser and the manufacturer.
Annex JA gives specification of hexagon nuts not given in ISO 4032 to ISO 4036, and ISO 8673 to ISO 8675, Annex JB gives specifications of steel nuts of property classes 4 t TO 10 T.
NOTE: The International Standards corresponding to this Standard and the symbol of degree of correspondence are as follows.
ISO 4032 : 2012 Hexagon regular nuts (style 1) - Product grades A andB
ISO 4033 : 2012 Hexagon high nuts (style 2) - Product grades A and B
ISO 4034 : 2012 Hexagon regular nuts (style 1) - Product grade C
ISO 4035 : 2012 Hexagon thin nuts chamfered (style 0) - Product grades A and B
ISO 4036 : 2012 Hexagon thin nuts unchamfered (style 0) - Product gradeB
ISO 8673 : 2012 Hexagon regular nuts (style 1) with metric fine pitch thread - Product grades A and B
ISO 8674 : 2012 Hexagon high nuts (style 2) with metric fine pitch thread - Product grades A and B
ISO 8675 : 2012 Hexagon thin nuts chamfered (style 0) with metric fine pitch thread - Product grades A and B (Overall evaluation: MOD)
In addition, symbols which denote the degree of correspondence in the contents between the relevant International Standards and JIS are IDT (identical), MOD (modified), and NEQ (not equivalent) according to ISOI lEC Guide 21-1.
| Screw Thread d |
| ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
|
| ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Screw Thread d |
| ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
|
| ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Screw Thread d |
| ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
|
|
Process flow
Cold forging
Annealing treatment(if need) ➨ wiredrawing ➨ clod forging ➨ tapping ➨make heat treatment(if need) ➨ Finish ➨ Packing
Hot forging
Cutting material ➨ hot forging ➨ turning ➨ tapping ➨ make heat treatment(if need) ➨ Finish ➨ Packing
Product Grade(Carbon steel)
Class 4T Class 5T Class 6T Class 8T Class 10T
Product Grade(Stainless Steel)
304 A2-70 A2-80 316 A4-70 A4-80
Materials and Chemical compstition
Carbon
1008
| CHEMICAL COMPOSI % | ||||||||
| C | Si | Mn | P | S | Cr | Ni | Cu | Al |
| 0.06 | 0.06 | 0.33 | 0.013 | 0.003 | 0.01 | 0 | 0.01 | 0.028 |
1035
| CHEMICAL COMPOSI % | |||||||
| C | Si | Mn | P | S | Cr | Ni | Cu |
| 0.34 | 0.13 | 0.73 | 0.012 | 0.002 | 0.02 | 0.01 | 0.02 |
10B21
| CHEMICAL COMPOSI % | ||||||
| C | Si | Mn | P | S | Cr | B |
| 0.2 | 0.04 | 0.81 | 0.017 | 0.007 | 0.017 | 0.0021 |
1045
| CHEMICAL COMPOSI % | |||||||
| C | Si | Mn | P | S | Cr | Ni | Cu |
| 0.45 | 0.23 | 0.58 | 0.014 | 0.006 | 0.057 | 0.008 | 0.016 |
40CR
| CHEMICAL COMPOSI % | |||||||
| C | Si | Mn | P | S | Cr | Ni | Cu |
| 0.4 | 0.21 | 0.54 | 0.015 | 0.008 | 0.95 | 0.02 | 0.02 |
35CRMO
| CHEMICAL COMPOSI % | ||||||||
| C | Si | Mn | P | S | Cr | Ni | Cu | Mo |
| 0.35 | 0.22 | 0.59 | 0.01 | 0.003 | 0.93 | 0.01 | 0.01 | 0.21 |
42CRMO
| CHEMICAL COMPOSI % | ||||||||
| C | Si | Mn | P | S | Cr | Ni | Cu | Mo |
| 0.42 | 0.27 | 0.92 | 0.013 | 0.004 | 1.01 | 0.03 | 0.04 | 0.2 |
Stainless Steel
| CHEMICAL COMPOSI(% ) | |||||||||
| Type | C | Si | Mn | P | S | Ni | Cr | Mo | Cu |
| ≤ | ≤ | ≤ | ≤ | ≤ | ≥ | ≥ | ≥ | ≈ | |
| 201Cu | 0.08 | 1.00 | 7.5-10 | 0.06 | 0.03 | 4.00-6.00 | 14.0-17.0 | 2.0-3.0 | |
| 201 | 0.15 | 1.00 | 8.50 | 0.06 | 0.03 | 3.50-5.50 | 16.0-18.0 | ||
| 202 | 0.15 | 1.00 | 7.5-10 | 0.06 | 0.03 | 4.00-6.00 | 17.0-19.0 | ||
| 301 | 0.15 | 1.00 | 2.00 | 0.045 | 0.03 | 5.00-8.00 | 16.0-18.0 | ||
| 302 | 0.15 | 1.00 | 2.00 | 0.045 | 0.03 | 8.00-10.0 | 17.0-19.0 | ||
| XM7 (302HQ) | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 8.50-10.5 | 17.0-9.00 | 3.0-4.0 | |
| 303 | 0.15 | 1.00 | 2.00 | 0.20 | ≥0.15 | 8.00-10.0 | 17.0-19.0 | ≤0.60 | |
| 304 | 0.07 | 1.00 | 2.00 | 0.035 | 0.03 | 8.00-10.0 | 18.0-20.0 | ||
| 304HC | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 8.00-10.0 | 17.0-19.0 | 1.0-3.0 | |
| 304M | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 8.50-10.0 | 18.0-20.0 | ||
| 316 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | |
| 316L (12Ni) | 0.03 | 1.00 | 2.00 | 0.045 | 0.03 | 12.0-15.0 | 16.0-18.0 | 2.0-3.0 | |
| 316L (10Ni) | 0.03 | 1.00 | 2.00 | 0.045 | 0.03 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | |
| 321 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 9.00-13.0 | 17.0-19.0 | Ti≤5*C% | |
| 2520 | 0.08 | 1.00 | 2.00 | 0.035 | 0.03 | 19.0-22.0 | 24.0-26.0 | ||
Finish
PLAIN ZP YZP BLACK HDG DACROMET GEOMET CHROME NICKEL AND SO ON
PACKING
QBH BULK
20-25KG/CTN,36CTNS/PALLET
20-30KG/BAGS,36BAGS/PALLET
ONE TON/BOXES
50KG/ IRON DRUM,12 IRON DRUMS/PALLET
QBH SMALL PACKING
Packing in small boxes according to customer’s requirements
Packing in plastic bag according to customer’s requirements
QBH PALLET TYPE
SOLID WOOD FUMIGATION PALLET
EURO Pallet
THREE SPLINT PALLET
WOODEN BOX
Annex JB(normative)
Mechanical properties of steel nuts—property classes 4T to 10T
According JIS HANDBOOK FASTENERS&SCREW THREADS 2018
From Page 1583 to Page 1591